摘要
Lead-free(K0.5-x/2Na0.5-x/2Lix)(Nb0.8Ta0.2)O3(KNLNT)and(K0.49-x/2Na0.49-x/2-LixCa0.01)(Nb0.8Ta0.2)O3(KNLNT-Ca)ceramics were prepared by a conventional ceramic processing.Structural analysis shows that the Ca^2+ doping takes the A site of ABO3 perovskite and decreases the phase transition temperature.Property measurements reveal that as a donor dopant,the Ca^2+ doping results in higher room-temperature dielectric constant,lower dielectric loss,and lower mechanical quality factor.In addition,the Ca^2+ doping does not change the positive piezoelectric coefficient d33,but increases the converse piezoelectric coefficient d 33*significantly.This is likely due to the increase in the relaxation,as well as the appearance of(CaNa/K·-VNa/K’)defect dipoles.