摘要
本文研究了烧结钕铁硼SC片经过不同条件热处理后微观组织的变化,开发一种SC片富Nd相评价方法。结果表明:SC片热处理后富Nd相发生变化,通过分析富Nd相的形貌、成分和体积比,可以确定最佳的SC片热处理条件,采用最佳条件热处理的SC片可以获得高性能的烧结磁体。
This article investigated the influence of annealing on microstructure of SC flakes in Nd-Fe-B sintered magnets,and developed an evaluation method for Nd-rich phase of strip casting flakes.The results showed that microstructure of SC flakes changed with different annealing processes.The optimum process could be found by analyzing the morphology,composition and volume ratio of Nd-rich phase.High performance sintered magnets could be prepared by using SC flakes with optimum annealing process.