采用水热法制备双钙钛矿催化剂Sr2FeNiO6,考察不同浓度KOH溶液(4 mol·L^-1、6 mol·L^-1、8 mol·L^-1、10 mol·L^-1、12 mol·L^-1、14 mol·L^-1)对催化剂性能的影响,利用X射线衍射、比表面积测定、程序升温还原和扫描电镜等对样品进行性能表征,并以催化甲烷燃烧为目标,考察催化剂催化性能。结果表明,矿化剂KOH浓度对样品性能影响较大,当浓度为10 mol·L^-1时,起燃温度最低,T10%为430℃;浓度为8 mol·L^-1时,样品比表面积最大,为19.0 m^2·g^-1,完全燃烧温度最低,T90%为610℃。
Doublel perovskite catalyst Sr2FeNiO6 was prepared by hydrothermal synthesis.The influence of KOH concentrations(4 mol·L^-1,6 mol·L^-1,8 mol·L^-1,10 mol·L^-1,12 mol·L^-1,14 mol·L^-1)on catalyst performance was investigated.The title catalysts were characterized by XRD,BET,H2-TPR and SEM techniques.The catalytic activity was evaluated in methane combustion.The results show that KOH concentration has great influence on the performance of catalysts.When KOH concentration is 10 mol·L^-1,the light-off temperature is the lowest and the conversion of 10%is obtained at 430℃.The catalyst Sr2FeNiO6 retains a specific surface area of 19.0 m^2·g^-1 and the conversion 90%is obtained at 610℃when the KOH concentration is 8 mol·L^-1.
作者
胡译文
陈晓宇
彭俊峰
解亚琼
郑建东
Hu Yiwen;Chen Xiaoyu;Peng Junfeng;Xie Yaqiong;Zheng Jiandong(College of Material and Chemical Engineering,Chuzhou University,Chuzhou 239000,Anhui,China)
出处
《工业催化》
CAS
2020年第1期36-39,共4页
Industrial Catalysis
基金
安徽省自然科学研究重点项目(KJ2017A412)
大学生创新项目(2019CXXL124)
关键词
催化剂工程
水热合成法
双钙钛矿
甲烷燃烧
催化活性
catalyst engineering
hydrothermal synthesis
double perovskites
methane combustion
catalytic activity