采用高温煅烧和溶胶-凝胶法结合的方法制备得到不同复合比的g-C3N4/TiO2复合纳米材料,通过FT-IR和SEM表征手段分析了样品的结构和形貌。同时研究了g-C3N4/TiO2复合催化剂在可见光下降解罗丹明B的催化活性。实验结果表明,质量比为30%的g-C3N4/TiO2复合催化剂的催化效果最佳,当光催化反应时间为210 min时,其降解率达到59.4%。
g-C3N4/TiO2 composite nanomaterials with different mass ratios were prepared by high-temperature calcination and sol-gel methods.The structure,morphology and element composition of the samples were analyzed by FT-IR and SEM.Meanwhile,the catalytic activity of g-C3N4/TiO2 composite catalyst in Rhodamine B was studied.The experimental results showed that the g-C3N4/TiO2 composite catalyst with a mass ratio of 30%had the best catalytic effect.When the photocatalytic reaction time was 210 min,the degradation rate reached 59.4%.
作者
白苗苗
安小康
马向荣
孟宇
BAI Miao-miao;AN Xiao-kang;MA Xiang-rong;MENG Yu(College of Chemistry and Chemical Engineering, Yulin University, Yulin 719000, China;Key Laboratory of Low Metamorphic Coal Clean Utilization,Yulin University,Yulin 719000,China)
出处
《榆林学院学报》
2020年第2期10-14,共5页
Journal of Yulin University
基金
陕西省自然科学基础研究计划资助项目(2019JQ-905)
陕西省科技厅创新人才推进计划项目(2018KJXX-078)
陕西省教育厅科研计划项目资助(19JS071)
陕西省高校科协青年人才托举计划资助(20180608)
陕西省科技资源开放共享平台项目(2019PT-18)
榆林市产学研合作项目(2016CXY-01)
榆林学院博士科研启动基金(No.17GK12,No.17GK13)
关键词
氮化碳
二氧化钛
光催化
罗丹明B
carbon nitride
titanium dioxide
photocatalysis
Rhodamine B