High ionic conductivity and superior interfacial stability of solid electrolytes at the electrodes are crucial factors for high-performance all-solid-state sodium batteries. Herein, a composite solid electrolyte Na3PS4-polyethylene oxide is synthesized by the solution-phase reaction method with an improved ionic conductivity up to 9.4 × 10-5 S/cm at room temperature. Moreover, polyethylene oxide polymer layer is wrapped homogeneously on the surface of Na3PS4 particles, which could effectively avoid the direct contact between Na3PS4 electrolyte and sodium metal, thus alleviate their side reactions. We demonstrate that all-solid-state battery SnS2/Na with the composite solid electrolyte Na3PS4-polyethylene oxide delivers an enhanced electrochemical performance with 230 m Ah/g after 40 cycles.
High ionic conductivity and superior interfacial stability of solid electrolytes at the electrodes are crucial factors for high-performance all-solid-state sodium batteries. Herein, a composite solid electrolyte Na3PS4-polyethylene oxide is synthesized by the solution-phase reaction method with an improved ionic conductivity up to 9.4 × 10-5 S/cm at room temperature. Moreover, polyethylene oxide polymer layer is wrapped homogeneously on the surface of Na3PS4 particles, which could effectively avoid the direct contact between Na3PS4 electrolyte and sodium metal, thus alleviate their side reactions. We demonstrate that all-solid-state battery SnS2/Na with the composite solid electrolyte Na3PS4-polyethylene oxide delivers an enhanced electrochemical performance with 230 m Ah/g after 40 cycles.
基金
funding support from 1000 Talent Plan program(NO.31370086963030)
research projects from Shandong Province(2018JMRH0211,2017CXGC1010 and 2016GGX104001)
Taishan Scholar Program(11370085961006)
the National Science Foundation of Shandong Province(ZR2017MEM002)
the Fundamental Research Funds of Shandong University(201810422046,2017JC010,2017JC042,and 2016JC005)。