摘要
Conversion-type reaction anode materials with high specific capacity are attractive candidates to improve lithium ion batteries(LIBs), yet the rapid capacity fading and poor rate capability caused by drastic volume change and low electronic conductivity greatly hinder their practical applications. To circumvent these issues, the successful design of yolk@shell Fe2 O3@C hybrid composed of a columnar-like Fe2O3 core within a hollow cavity completely surrounded by a thin, self-supported carbon(C) shell is presented as an anode for high-performance LIBs. This yolk@shell structure allows each Fe2O3 core to swell upon lithiation without deforming the carbon shell. This preserves the structural and electrical integrity against pulverization, as revealed by in situ transmission electron microscopy(TEM) measurement. Benefiting from these structural advantages, the resulting electrode exhibits a high reversible capacity(1013 m Ah g-1 after80 cycles at 0.2 A g-1), outstanding rate capability(710 m Ah g-1 at 8 A g-1) and superior cycling stability(800 m Ah g-1 after 300 cycles at 4 A g-1). A Li-ion full cell using prelithiated yolk@shell Fe2 O3@C hybrid as the anode and commercial Li CoO2(LCO) as the cathode demonstrates impressive cycling stability with a capacity retention of 84.5% after 100 cycles at 1 C rate, holding great promise for future practical applications.
Conversion-type reaction anode materials with high specific capacity are attractive candidates to improve lithium ion batteries（LIBs）, yet the rapid capacity fading and poor rate capability caused by drastic volume change and low electronic conductivity greatly hinder their practical applications. To circumvent these issues, the successful design of yolk@shell Fe2 O3@C hybrid composed of a columnar-like Fe2O3 core within a hollow cavity completely surrounded by a thin, self-supported carbon（C） shell is presented as an anode for high-performance LIBs. This yolk@shell structure allows each Fe2O3 core to swell upon lithiation without deforming the carbon shell. This preserves the structural and electrical integrity against pulverization, as revealed by in situ transmission electron microscopy（TEM） measurement. Benefiting from these structural advantages, the resulting electrode exhibits a high reversible capacity(1013 m Ah g-1 after80 cycles at 0.2 A g-1), outstanding rate capability(710 m Ah g-1 at 8 A g-1) and superior cycling stability(800 m Ah g-1 after 300 cycles at 4 A g-1). A Li-ion full cell using prelithiated yolk@shell Fe2 O3@C hybrid as the anode and commercial Li CoO2（LCO） as the cathode demonstrates impressive cycling stability with a capacity retention of 84.5% after 100 cycles at 1 C rate, holding great promise for future practical applications.
基金
supported by the National Natural Science Foundation of China(Grants No.21703185)
the leading Project Foundation of Science Department of Fujian Province(Grants No.2018H0034)
Fundamental Research Funds for the Central Universities(Xiamen University:20720170042)
the“Double-First Class”Foundation of Materials and Intelligent Manufacturing Discipline of Xiamen University。