摘要
The emergence of non-fullerene acceptors(NFA) offers a promising opportunity to develop high-performance donor/acceptor pairs with high power conversion efficiency,as NFAs offer tunable energy levels,broad absorption and suitable aggregation property.In order to enhance light-harvesting capability of active layers,we choose a wide bandgap polymer PTQ10 as the donor to blend with a narrow bandgap NFAY6 as the acceptor.In comparison with PTQ10:IDIC blend,~130 nm red-shifted absorption spectrum is observed in the PTQ10:Y6 blend,which potentially enhance the short-circuit current density(Jsc) for the PSCs.In addition,the optimal PTQ10:Y6 blend shows higher photoluminescence quenching efficiency and more efficient charge separation,higher charge mobilities,as well as weaker bimolecular recombination over the PTQ10:IDIC blend,which leads to an outstanding power conversion efficiency(PCE) of 16.53%,with a notable Jsc of 26.65 mA cm^-2 and fill factor(FF) of 0.751.
The emergence of non-fullerene acceptors（NFA） offers a promising opportunity to develop high-performance donor/acceptor pairs with high power conversion efficiency,as NFAs offer tunable energy levels,broad absorption and suitable aggregation property.In order to enhance light-harvesting capability of active layers,we choose a wide bandgap polymer PTQ10 as the donor to blend with a narrow bandgap NFAY6 as the acceptor.In comparison with PTQ10:IDIC blend,～130 nm red-shifted absorption spectrum is observed in the PTQ10:Y6 blend,which potentially enhance the short-circuit current density(Jsc) for the PSCs.In addition,the optimal PTQ10:Y6 blend shows higher photoluminescence quenching efficiency and more efficient charge separation,higher charge mobilities,as well as weaker bimolecular recombination over the PTQ10:IDIC blend,which leads to an outstanding power conversion efficiency（PCE） of 16.53%,with a notable Jsc of 26.65 mA cm-2 and fill factor（FF） of 0.751.
基金
supported by the National Natural Science Foundation of China(51873140,51603136,91633301)