为解决纸基绝缘材料散热不足的问题,本研究利用3-氨丙基三乙氧基硅烷(APTES)对六方氮化硼(h-BN)填料进行表面改性处理后,添加到纸浆纤维中制备具有良好热传导性能和绝缘性能的导热氮化硼复合绝缘纸。研究结果表明,APTES对h-BN改性成功且改性h-BN导热填料热稳定性略有下降;当混合尺寸改性h-BN导热填料添加量为40 wt%时,绝缘纸的导热系数和体积电阻率分别为0.682 W/(m·K)和4.72×1014Ω·cm,比原纸分别提高了387%和84.4%。
In this study,boron nitride composite insulation paper with improved thermal conductivity and electrical insulation properties were produced by mixing pulp fiber,and h-BN which was modified by 3-amopropyl triethoxy silane(APTES).The results showed that the modification of APTES to h-BN was successful and thermostability of the modified h-BN decreased slightly.When h-BN content was 40 wt%,the thermal conductivity and volume resistivity of the composite insulation paper was 0.682 W/(m·K)and 4.72×1014Ω·cm,respectively,a 387%and 84.4%increase compared with that of control paper sample.Therefore,h-BN composite insulation paper had a potential application in the fields of power and electronic.
作者
王秀
俞智怀
房桂干
吴伟兵
戴红旗
WANG Xiu;YU Zhihuai;FANG Guigan;WU Weibing;DAI Hongqi(Jiangsu Co-Innovation Center of Efficient Processing and Utilization of Forest Resources,Nanjing Forestry University,Nanjing,Jiangsu Province,210037;Research Institute of Chemical Processing and Utilization of Forest Products,CAF,Nanjing,Jiangsu Province,210042)
出处
《中国造纸学报》
CAS
CSCD
北大核心
2019年第4期7-13,共7页
Transactions of China Pulp and Paper
基金
“十三五”国家重点研发计划课题(2017YFD0601005)
国家自然科学基金项目(31470599)
关键词
纸浆纤维
六方氮化硼
表面改性
导热性能
绝缘性能
boron nitride composite insulation paper
h-BN
surface modification
thermal conductivity
insulation performance