In-situ synthesized ceramic such as TiC,Cr7C3 and Cr5B3 reinforced Ni-based alloy composite coating was fabricated on the surface of mild steel substrate by reactive braze coating processing with colloidal graphite,Cr,Ni,ferro-boron,Si and titanium powders as the raw materials at low temperature of 1000℃,and a new kind of coating materials was developed.By means of SEM,EDS,XRD and surface hardness tester,the microstructures,phases,hardness and wear-resistance of the coating were analyzed,respectively.The results revealed that the coating was mainly composed of the ceramic in-situ synthesized reinforcement phases of TiC,Cr7C3 and Cr5B3 and the binder phases in-situ synthesized of Ni31Si12 and(Ni,Fe)solid solution;The ceramic reinforcement phases of TiC,Cr7C3 and Cr5B3 were randomly distributed in the binder phases of Ni31Si12 and(Ni,Fe)solid solution;The coating had about 15vol%pores and can possibly be applied as a self-lubrication coating;The coating and the substrate were integrated together by metallurgical bonding;The coating had a hardness up to 91-94HR15N.
基金
supported by Yangjiang science and technology project (0202010067)
Yangjiang polytechnic for providing financial assistance.