摘要
Pore size and distribution in carbon-based materials are regarded to be a key factor to affect the electrochemical capacitive performances of the resultant electrodes.In this study,nitrogen and oxygen codoped porous carbons(NOPCs) are fabricated based on a simple Schiff-base reaction between m-phenylenediamine and terephthalaldehyde.The NOPCs have tunable morphologies,high surface areas,abundant heteroatom doping.More importantly,the carbons show a dominant micropores of 0.5-0.8 nm,comparable to the ionic sizes of LiTFSI(Li^+0.069 nm;TFSI-0.79 nm) water-in-salt electrolyte with a high potential window of 2.2 V.Consequently,the fabricated symmetric supercapacitor gives a high energy output of 30.5 Wh/kg at 1 kW/kg,and high stability after successive 10,000 cycles with ^96.8% retention.This study provides promising potential to develop high-energy supercapacitors.
Pore size and distribution in carbon-based materials are regarded to be a key factor to affect the electrochemical capacitive performances of the resultant electrodes.In this study,nitrogen and oxygen codoped porous carbons(NOPCs) are fabricated based on a simple Schiff-base reaction between m-phenylenediamine and terephthalaldehyde.The NOPCs have tunable morphologies,high surface areas,abundant heteroatom doping.More importantly,the carbons show a dominant micropores of 0.5-0.8 nm,comparable to the ionic sizes of LiTFSI(Li^+0.069 nm;TFSI-0.79 nm) water-in-salt electrolyte with a high potential window of 2.2 V.Consequently,the fabricated symmetric supercapacitor gives a high energy output of 30.5 Wh/kg at 1 kW/kg,and high stability after successive 10,000 cycles with ～96.8% retention.This study provides promising potential to develop high-energy supercapacitors.
基金
financially supported by the National Natural Science Foundation of China(Nos.21875165,51772216 and 21703161)
the Science and Technology Commission of Shanghai Municipality,China(No.14DZ2261100)
the Fundamental Research Funds for the Central Universities。