Electrospun Sb2Se3@C nanofibers with excellent lithium storage properties

Antimony-based materials have become promising anodes within lithium-ion batteries(LIBs)due to their low cost and the high theoretical capacity.However,there is a potential to further enhance the electrochemical performance of such antimony-based materials.Herein,Sb2Se3@C nanofibers(Sb2Se3@CNFs)are designed and obtained via a novel electrospinning method.Upon electrochemically testing as an anode within LIBs,the Sb2Se3@CNFs(annealed at 600℃)delivers a remarkably good cycling performance of 625 mAh/g at 100 mA/g after 100 cycles.Moreover,it still remains at 490 mAh/g after 500 cycles with an applied current density of 1.0 A/g.The excellent performance of the Sb2 Se3@CNFs can be attributed to the fact that the N-doped C matrices not only remit the volume expansion of materials,but also enhance the electrical and ionic conductivity thusly increasing the lithium-ion diffusion.The obtained Sb2Se3@CNFs are promising anode for LIBs in the future.