氨水储槽泄漏的粘接修复

The Bonding Repair Process of Ammonia Storage Tank

阐述了氨水储槽破裂的原因及粘接修复工艺过程。破裂部位在经过清洗打磨,18%的浓盐酸处理液中室温处理5~10 min后,选用无碱无蜡玻璃纤维布和环氧-聚硫胶为修复材料,采用涂胶与玻璃布贴敷交替进行,最后室温固化24 h,完成整个粘接修复过程。

The reason of rupture for the Ammonia storage tank,and the bonding repair process is introduced. After cleaned and polished,the rupture is treated in the 18% hydrochloric acid for 5 ~ 10 min at room temperature. The glass fiber cloth and the epoxy-polysulfide resin adhesive are used as the repairing materials,glue and glass cloth are applied alternately,finally cured for 24 hours in the room temperature,and the bonding repair process of the Ammonia storage tank is completed.