摘要
A 6061 Al coating for AZ31 Mg alloy was prepared by multi-pass friction stir welding(FSW)with different travel speeds.The mi-crostructure,mechanical properties of the interfacial region and the corrosion behavior of the coating were investigated systematically.The results indicate that the interfacial intermetallic compounds formed in the stir zone(SZ)consist of mainly Al12Mg17 and Al3Mg2.The inter-metallic compounds in the SZ are significantly increased when the travel speed is increased from 30 mm/min to 60 mm/min.Microhardness measurements and results of shear-tensile tests show that the mechanical properties are influenced by the intermetallic compounds formed in the SZ during FSW.Corrosion tests indicate that the 6061 Al coating can significantly improve the corrosion resistance of AZ31 plate.The 6061 Al coating obtained with a travel speed of 30 mm/min has a maximum corrosion potential E corr of-0.503 V VSE.
基金
The authors acknowledge financial support by the National Natural Science Foundation(Project No.51601024)
the National Key Research and Development Program of China(Project No.2016YFB0700403)
the Chongqing Research Program of Basic Research and Frontier Technology(Project No.cstc2019jcyj-msxmX0306)
the Fundamental Research Funds for the Central Universities(Project Nos.2019CDXYCL0031,2018CDJDCL0019,2018CDJDCD0001,and 2018CDGFCL0005)
the support of the 111 Project(Project No.B16007)by the Ministry of Education and the State Administration of Foreign Experts Affairs of China.