6063铝合金双道次热变形微观组织演变 被引量:5

Microstructure evolution of 6063 aluminum alloy during double-pass hot deformation
原文传递
导出
摘要 采用Gleeble-1500热模拟试验机对6063铝合金进行双道次热轧试验,分析了合金在变形温度为300~500℃,应变速率为0. 001~0. 1 s^-1,道次间停留时间10~90 s时的流变应力和微观组织。结果表明:随着道次间停留时间增长,第二道次屈服应力减小;温度与道次间停留时间对合金的静态软化率有较大的影响。低温大应变速率短道次间停留时间下试样的强化相较多,其形貌为长条状与圆形;高温低应变速率长道次间停留时间下试样的强化相数量有所减少,其形貌以圆形为主。通过能谱分析可知,试样中的强化相以AlFeSi为主,长条状强化相为6μm左右,圆形强化相尺寸约2μm。 Double-pass hot rolling test on 6063 aluminum alloy was carried out by using Gleeble-1500 thermal simulator. Flow stress and microstructure of the alloy when the deformation temperature was 300-500 ℃,the strain rate was 0. 001-0. 1 s^-1 and the residence time between passes was 10-90 s were analyzed. The results show that the yield stress of the second pass decreases with the increase of the residence time between passes,and the static softening rate of the alloy is affected by the temperature and the residence time between passes.There is more strengthening phase in the double-pass hot rolled alloy under the condition of low temperature,high strain rate and short residence time between passes,which morphology is mainly strip and round,however,when under the condition of high temperature,low strain rate and long residence time between passes,the content of the strengthening phase decreases and its morphology is mainly round.Besides,the strengthening phase in the alloy is mainly Al Fe Si phase,and the strip-like phase has a length of about 6 μm and the round phase has a size of about 2 μm.
作者 王冠 田昌龄 寇琳媛 卞东伟 Wang Guan;Tian Changling;Kou Linyuan;Bian Dongwei(School of Mechanical Engineering,Ningxia University,Yinchuan Ningxia 750021,China;The Key Laboratory of CAE Technology for Intelligent Equipment,Ningxia University,Yinchuan Ningxia 750021,China;College of Mechatronics Engineering,Henan University of Science and Technology,Luoyang Henan 471003,China)
出处 《金属热处理》 CAS CSCD 北大核心 2020年第5期23-28,共6页 Heat Treatment of Metals
基金 国家自然科学基金(51605234) 宁夏自然科学基金(2018AAC03061,2019AAC03031) 宁夏重点研发计划项目(西部之光2017) 西部一流重大创新项目(ZKZD2017010)。
关键词 6063铝合金 双道次 热压缩 流变应力 微观组织 6063 aluminum alloy double-pass hot compression flow stress microstructure
  • 相关文献

参考文献4

二级参考文献25

  • 1DAVID A L,RAY M H.Strong aluminum alloy shaves air frame weight[J].Advanced Materials&Processes,1991,140(4):46-52.
  • 2CHEN K H,LIU H W,ZHANG Z,LI S,TODD R I.The improvement of constituent dissolution and mechanical properties of 7055 aluminum alloy by stepped heat treatments[J].Journal of Materials Processing Technology,2003,142(1):190-196.
  • 3CHANDAN M,MUKHOPADHYAY A K,RAGHU T,VARMA K.Tensile properties of peak aged 7055 aluminum alloy extrusions[J].Materials Science and Engineering A,2007,455(25):673-680.
  • 4SHERCLIFF H R,LOVATT A M,JENSEN D J,BEYNON J H.Modeling of microstructure evolution in hot deformation[J].Philosophical Transactions:Mathematical,Physical and Engineering Sciences,1999,357(1756):1621-1643.
  • 5RICKS R A,HOWE A,BROWN L M,BEYNON J H,HANSEN N.The deformation models needed by the aluminum industry[J].Philosophical Transactions:Mathematical,Physical and Engineering Sciences,1999,357(1756):1513-1529.
  • 6ROBSON J D.Micro-structural evolution in aluminum alloy 7050 during processing[J].Materials Science and Engineering A,2004,382:112-121.
  • 7KOCKS U F,MECKING H.Physics and phenomenology of strain hardening:the FCC case[J].Progress in Materials Science,2003,48(2):171-273.
  • 8KIM H,KANG S,TSUJI N,MINAMINO Y.Elongation increase in ultra-fine grained Al-Fe-Si alloy sheets[J].Acta Materialia,2005,53(6):1737-1749.
  • 9HU H E,ZHEN L,YANG L,SHAO W Z,ZHANG B Y.Deformation behavior and microstructure evolution of 7050 aluminum alloy during high temperature deformation[J].Materials Science and Engineering A,2008,488(3):64-71.
  • 10FURU T.The influence of transient deformation conditions on recrystallization during thermomechanical processing of an Al-1%Mg alloy[J].Acta Materialia,1999,47(5):2377-2389.

共引文献22

同被引文献55

引证文献5

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部