改性环氧树脂砂基透水砖性能研究 被引量:5

Study on properties of modified resin sand-based permeable brick
下载PDF
导出
摘要 采用偶联剂、石灰石粉、纳米超细氧化物对环氧树脂砂基透水砖进行改性,试验结果表明:不同种类偶联剂对环氧树脂砂基透水砖均有增强作用,偶联剂的最佳用量为树脂质量的5%,石灰石粉和纳米超细氧化物对环氧树脂砂基透水砖具有一定的增强效果;当硅烷偶联剂和纳米SiO2的用量分别为环氧树脂质量的5%、2%,环氧树脂用量为覆膜砂质量的4%时,树脂砂基透水砖的强度和耐磨性能最佳,抗压强度为37.8 MPa,耐磨性为22 mm,此时透水速率为4.3 m L/(min·cm^2)。 Resin sand-based permeable brick was modified by coupling agent,limestone powder and nano-fine oxide.The results show that different kinds of coupling agents can enhance the strength of resin sand-based permeable bricks,the optimum dosage of different kinds of coupling agents is 5%of the weight of the resin.Limestone powder and nano-ultrafine oxide have certain enhancement effect on the strength of resin sand-based permeable bricks.When the dosage of silane coupling agent and nano-SiO2 is 5%and 2%of the mass of epoxy resin respectively,and the dosage of epoxy resin is 4%of the mass of coated sand,the strength and wear resistance of resin sand-based permeable bricks are the best.Compressive strength is 37.8 MPa,wear resistance is 22 mm,and the permeation rate is 4.3 mL/(min·cm^2).
作者 张建强 姜建松 习海平 柴天红 刘桂平 黄沙 ZHANG Jianqiang;JIANG Jiansong;XI Haiping;CHAI Tianhong;LIU Guiping;HUANG Sha(Jiangxi Institute of Scientific Research and Design of Building Materials Industry,Nanchang 330001,China)
出处 《新型建筑材料》 北大核心 2020年第6期132-134,共3页 New Building Materials
基金 江西省科技计划重点研发领域一般项目(20171BBG70079)。
关键词 海绵城市 砂基透水砖 表面改性剂 石灰石粉 纳米超细氧化物 sponge city sand-based permeable brick surface modification agent limestone powder nano-ultrafine oxide
  • 引文网络
  • 相关文献

参考文献6

二级参考文献18

共引文献531

同被引文献67

引证文献5

二级引证文献7

;
使用帮助 返回顶部