铝电解过程阳极气泡的析出行为 被引量:4

Behavior of Anodic Bubbles Precipitation in Aluminum Electrolytic Process
下载PDF
导出
摘要 铝电解过程阳极生成的气泡在排放过程中的运动带动电解质的流动,其流动行为影响氧化铝的溶解和金属的二次反应,对电解过程影响较大。采用透明槽进行铝电解实验,用高速照相机和摄像机记录电解过程中的气泡行为并进行分析。结果表明,气泡的生成分为两个阶段。第一个阶段为气泡在阳极底部的生长,第二个阶段为气泡脱离阳极底部在电解质中上升。在阳极电流密度0.7 A/cm^2下电解,在气泡生长阶段,阳极底部气泡层的最大厚度为0.4 cm,气泡生长到最大需要的时间为12 s,气泡脱离阳极底部在电解质中上升需要的时间为0.27 s。整个电解过程,阳极侧部小气泡不断长大、逸出。采用Matlab数学处理软件,用直方图均衡化方法处理摄像机拍摄的实验图像,可获得阳极侧壁气泡生成的清晰图像,用于深入观察和分析气泡的析出行为。 The movement of anode bubbles in aluminum electrolysis cell is the main force of electrolyte flow.Its flow behavior affects the dissolution of alumina and the secondary reaction of metals,and has a greater influence on the electrolytic process.In this paper,the bubbles behavior of aluminum electrolytic cell is recorded by high speed camera and camera through the aluminum electrolysis experiment in transparent electrolytic cell.The results show that there are two stages of bubbles behavior.The first stage is the growth stage of the bubbles at the bottom of the anode,the second stage is the stage of the bubbles rising from the bottom of the anode in the electrolyte.The electrolysis is carried out at an anode current density of 0.7 A/cm^2.It takes about 12 s for bubbles growth to the maximum thickness of 0.4 cm at first stage,and it takes 0.27 s for the bubbles escape from anode bottom to electrolyte free surface at second stage.Small bubbles on the anode sidewall grow up and escape continuously during the whole electrolysis process.The experimental images taken by cameras are processed by the histogram equalization method in Matlab.Clear images of the bubbles generated on the anode sidewall can be obtained for in-depth observation and analysis of the bubbles precipitation behavior.
作者 李松 石忠宁 赵志彬 LI Song;SHI Zhongning;ZHAO Zhibin(School of Chemical and Materials Engineering,Liupanshui Normal University,Liupanshui 553000,China;School of Metallurgy,Northeastern University,Shenyang 110819,China;Shenyang Aluminum and Magnesium Engineering and Research Institute,Shenyang 110001,China)
出处 《有色金属工程》 CAS 北大核心 2020年第6期53-57,96,共6页 Nonferrous Metals Engineering
基金 贵州省教育厅自然科学项目(黔教合KY字[2017]273) 六盘水师范学院重点学科建设项目(LPSSYZDXK201708) 六盘水师范学院科技创新团队项目(LPSSYKJTD201801,LPSSYKJTD201905) 六盘水市重点实验室项目(52020-2018-03-04,52020-2019-05-09) 六盘水市科技创新团队项目(52020-2019-05-08)。
关键词 铝电解 阳极 气泡 aluminum electrolysis anode gas bubbles
  • 相关文献

参考文献3

二级参考文献24

  • 1CHEN Zhuo 1,MEI Chi 1,CHEN Hong-rong 1,MO Jiao 2 (1 Institute on Simulation and Optimization of Pyro-installation, Central Sout h University, Changsha 410083, China,2 Science School, Beijing University of Posts and Telecommunications, Beijing 1.Simulation of moving boundary of the reaction shaft in a flash smelting furnace[J].Journal of Central South University,2001,13(3):213-218. 被引量:4
  • 2薛玉卿,周乃君,包生重.铝电解槽内阳极气泡运动的冷态模拟[J].中国有色金属学报,2006,16(10):1823-1828. 被引量:17
  • 3[1]Sadoway D R.Inert anodes for the Hall-Héroult cell:the ultimate materials challenge[J].JOM,2001,53(5):34-35.
  • 4[2]Sekhar J A,Liu J.Non-consumable anode materials [A].Welch B.Light Metals [C].Warrendale:TMS,1998.597-603.
  • 5[3]Pawlek R P.Inert anodes for the primary aluminium industry[A].Hale W.Light Metals [C].Warrendale:TMS,1996.243-248.
  • 6[4]Beck T R.A non-consumable metal anode for production of aluminum with low temperature fluoride melts[A].Evans J.Light Metals [C].Warrendale:TMS,1995.355-360.
  • 7[6]Grjotheim K,Kvande H,QIU Zhu-xian,et al.Interfacial phenomena in molten salt selctrolysis[J].Aluminium,1989,65(2):157-162.
  • 8[7]Laszlo J K,Sandor P.Effect of the bubble growth mechanism on the spectrum of voltage fluctuations in the reduction cell[A].Sclmeider W.Light Metals [C].Warrendale:TMS,2002.365-370.
  • 9[8]Xue J,Oye H.Bubble behaviour-cell voltage oscillation during aluminium electrolysis and the effects of sound and ultrasound[A].Evans J.Light Metals [C].Warrendale:TMS,1995.265-270.
  • 10[9]Hyde T H,Welch B J.The gas under anodes in aluminum smelting cells(part Ⅰ):Measuring and modelling bubble resistance under horizontally oriented electrodes[A].Huglen R.Light Metals [C].Warrendale:TMS,1997.333-340.

共引文献21

同被引文献45

引证文献4

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部