Irradiation makes structural materials of nuclear reactors degraded and failed.However,the damage process of materials induced by irradiation is not fully elucidated,mostly because the charged particles only bombarded the surface of the materials(within a few microns).In this work,we investigated the effects of surface irradiation on the indirect irradiation region of the(Al0.3Cr0.2Fe0.2Ni0.3)3O4 high entropy oxide(HEO)films in detail by plasma surface interaction.The results show that the damage induced by surface irradiation significantly extends to the indirect irradiation region of HEO film where the helium bubbles,dislocations,phase transformation,and the nickel oxide segregation were observed.
作者
张健聪
孙森
杨朝明
裘南
汪渊
Jian-Cong Zhang;Sen Sun;Zhao-Ming Yang;Nan Qiu;Yuan Wang(Key Laboratory of Radiation Physics and Technology,Ministry of Education,Institute of Nuclear Science and Technology,College of Physics,Sichuan University,Chengdu 610064,China)
基金
National Key Research and Development Program of China(Grant No.2017YFB0405702)
the National Natural Science Foundation of China(Grant No.11775150).