摘要
以连铸生产线用后MgO-Y2O3复合稳定氧化锆(以下简称为(Mg,Y)-PSZ)质定径水口残样为研究对象,通过X射线衍射仪对其原砖层、过渡层和变质层的物相组成进行检测,并通过扫描电镜和电子探针对各层的显微结构和微区化学组成进行观察和分析,研究了连铸过程中钢渣侵蚀对氧化锆质定径水口组成和结构的影响,在此基础上研究氧化锆质定径水口晶粒损毁过程和机制。
A residual sample of a MgO-Y2O3 composite stabilized zirconia metering nozzle after continuous casting was used as research objects,and the phase composition of the original brick layer,the transition layer and the corrosion layer were detected by X-ray diffraction.The microstructure and the micro-area chemical composition of the layers were observed and analyzed by a scanning electron microscope and an electron probe.The effect of the steel slag corrosion on the phase composition and microstructure of the zirconia metering nozzle during the continuous casting was studied.Based on this,the process and mechanism of the grain fracture in the zirconia metering nozzle were studied.
作者
赵亮
薛群虎
张晗
李翔
姚爽
Zhao Liang;Xue Qunhu;Zhang Han;Li Xiang;Yao Shuang(School of Civil and Architectural Engineering,Yangtze Normal University,Chongqing 408100,China;不详)
出处
《耐火材料》
CAS
北大核心
2020年第4期322-325,329,共5页
Refractories
基金
国家自然科学基金面上项目(51372193)
重庆市教委科学技术研究项目(KJQN201901412)。
关键词
部分稳定氧化锆
稳定剂
钢渣
晶粒
破裂
损毁机制
partially stabilized zirconia
stabilizing agent
steel slag
crystal grain
fracture
damage mechanism