A new long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(PPO)/polybenzimidazole(PBI)amphoteric membrane for vanadium redox flow battery

A new amphoteric membrane was prepared by blending long-side-chain sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(S-L-PPO)and polybenzimidazole(PBI)for vanadium redox flow battery(VRFB)application.An acid-base pair structure formed between the imidazole of PBI and sulfonic acid of S-L-PPO resulted in lowered swelling ratio.It favors to reduce the vanadium permeation.While,the increased sulfonic acid concentration ensured that proton conductivity was still at a high level.As a result,a better balance between the vanadium ion permeation(6.1×10^-9 cm^2·s^-1)and proton conductivity(50.8 m S·cm^-1)in the S-L-PPO/PBI-10%membrane was achieved.The VRFB performance with S-L-PPO/PBI-10%membrane exhibited an EE of 82.7%,which was higher than those of pristine S-L-PPO(81.8%)and Nafion 212(78.0%)at 120 m A·cm^-2.In addition,the S-LPPO/PBI-10%membrane had a much longer self-discharge duration time(142 h)than that of Nafion 212(23 h).