在653~693K温度下电解LiCl-KCl体系制备金属锂,分别研究电解温度、电流密度、电解质比例以及阴阳极间距对金属锂电解电流效率的影响。最佳电解温度为653~673K、LiCl-KCl电解质最佳质量比为LiCl∶KCl=50%∶50%,同时较大的电流密度与极距对电流效率更有利。
Lithium metal was produced from LiCl-KCl molten salt at 653-693 Kby molten salt electrolysis.Effects of electrolysis temperature,current density,electrolyte ratio,and inter-electrode distance on current efficiency of lithium metal electrolysis are analyzed.The results show that the optimum electrolysis temperature is 653-673 K,the optimum mass ratio of LiCl-KCl electrolyte is 50%∶50%,and higher current density and pole distance is beneficial to current efficiency.
作者
张松岩
朱实贵
路贵民
ZHANG Song-yan;ZHU Shi-gui;LU Gui-min(Engineering Research Center of Resource Process Engineering,Ministry of Education,East China University of Science and Technology,Shanghai 200030,China;National Engineering Research Center for Integrated Uilization of Salt Lake Resource,Shanghai 200030,China;Fengxin Ganfeng Lithium Industry Co.,Ltd.,Yichun 336000,Jiangxi,China)
出处
《有色金属(冶炼部分)》
CAS
北大核心
2020年第8期47-50,共4页
Nonferrous Metals(Extractive Metallurgy)
基金
国家重点研发计划项目(2018YFC0604806)。
关键词
金属锂
熔盐电解
电流效率
工艺条件
lithium metal
molten salt electrolysis
current efficiency
technological condition