Precipitation and evolution of nodular graphite during solidification process of ductile iron 被引量:6

下载PDF
导出
摘要 The quantity and morphology of spheroidal graphite have an important effect on the properties of ductile iron, and the characteristics of spheroidal graphite are determined by the solidification process. The aim of this work is to explore the precipitation and evolution of graphite nodules in hypoeutectic, eutectic, and hypereutectic ductile irons by thermal analysis, liquid quenching and metallographic technique. Results show that hypoeutectic ductile iron has the longest solidification time and the lowest eutectic temperature;eutectic ductile iron has the shortest solidification time;hypereutectic ductile iron has the highest eutectic temperature. After solidification is completed, hypoeutectic ductile iron has the lowest nodule count, nodularity and graphite fraction;eutectic ductile iron has the highest nodule count, nodularity and the smallest nodule diameter;hypereutectic has the highest nodule diameter and graphite fraction. The nucleation and growth of graphite nodules in hypereutectic ductile iron starts before bulk eutectic crystallization stage, however, the precipitation and evolution of graphite nodules of hypoeutectic and eutectic ductile irons mainly occur in the eutectic crystallization stage. The graphite precipitated in eutectic crystallization of hypoeutectic, eutectic, and hypereutectic ductile irons, are 61%, 68% and 43% of total graphite volume fraction, respectively. Simultaneously, there are plenty of austenite dendrites in hypoeutectic and hypereutectic ductile irons, which are prone to shrinkage defects. Therefore, the eutectic ductile iron has the smallest shrinkage tendency.
出处 《China Foundry》 SCIE 2020年第4期260-271,共12页 中国铸造(英文版)
基金 This work was financially supported by the National Natural Science F oundation of China(NSFC)under Grant Nos.51601054 and 51775006 the Natural Science Foundation of Hebei Province of China under Grant Nos.E2017202095 and E2016202100 the Scientific and Technological Transformative Project of Tianjin Supporting Bijing-Tianjin-Hebei under Grant No.18YFCZZC00030 the Central Government Guides I.ocal Science and Technology Development Fund Projects under Grant No.206Z 1005G.
  • 相关文献

参考文献8

二级参考文献66

  • 1盛达.蠕墨铸铁的起源、发展及其熔炼工艺[J].现代铸铁,2009,29(5):20-26. 被引量:9
  • 2刘炀.石墨钢轧辊的悬浮铸造工艺研究[J].热加工工艺,2004,33(7):43-44. 被引量:2
  • 3李玲芳,舒信福,李玉中,朱延东.锰铜合金化贝氏体低碳球墨铸铁[J].现代铸铁,2005,25(6):14-16. 被引量:1
  • 4吴晓俊,邢建东,符寒光,智小慧.高铬白口铸铁初生碳化物细化的研究进展[J].铸造,2006,55(10):999-1003. 被引量:18
  • 5Daris J R. Cast Irons. In: ASM Specialty Handbook, ASM International Materials Park, OH, 1996.
  • 6Stefanescu D M. Castlron. In: Metals Handbook, 9th ed., ASM, Metal Park, OH, 1988(15):168-181.
  • 7Steeb S, Maier U. The Molten Structure of Fe-C Alloys, The Metallurgy of Cast Iron, ed. by B. Lux, I. Minkoff and F. Mollard. In: Proc. 2nd Int. Symp. on the Physical Metallurgy of Cast Iron. St Saphorin: Georgi Publishing Company, Switzerland,1975.
  • 8Benecke T, Ta A T, Kahr G, Schubert W D and Lux B. Aufloseverhalten und Vorimpfeffekt von SiC in Gusseisenschmelzen. Giesserei, 1987(10 /11): 301-306.
  • 9Худокормов Д Н, Калиниченко А С, Жвавый Н П. Испольэованне Быстроохлажденного Модификатора для устранения Отбела в Чугуне. Литеиное Проиэводство, 1989 (12): 9-10.
  • 10Margerie J C. The Notion of Heredity in Cast Iron Metallurgy, The Metallurgy of Cast Iron, ed. by B. Lux, I. Minkoff and F. Mollard. In: Proc. 2nd Int. Syrup. on the Physical Metallurgy of Cast Iron. St Saphorin: Georgi Publishing Company, Switzerland,1975: 545-558.

共引文献24

同被引文献30

引证文献6

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部