Mechanical Properties, Crystallization and Biodegradation Behavior of the Polylactide/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate)/ Poly(butylene adipate-co-terephthalate) Blown Films

Polactide(PLA),poly(3-hydroxybutyrate-co-4-hydroxybutyrate)(P(3HB-CO-4HB)),and poly(butylene adipate co-terephthalate)(PBAT)ternary blends were prepared by extrusion blending.The biodegradable PLA/P(3HB-co 4HB)/PBAT films were successfully obtained by using blown films technique.Excellnt siffness-toughness balance was achieved for 55/10/35 PLA/P(3HB-co 4HB)/PBAT film.The tensile strength reached 33.0 MPa(MD)and 23.5 MPa(TD).the elongation at break exceeded 1309%,and tear strength exceeded 110 kN/m.The Young's modulus as low as about 1800 MPa also met packaging applications.SEM observations revealed rough and long ligaments,indicating that the tear specimens were broken yieldingly.The addition of PBAT elastomers was the main reason for the improved toughness of the film.From DMA and SEM analysis,it was demonstrated that PLA P(3HB co 4HB),and PBAT were prilly compatible.With increasing P(3HB CO-4HB)content,the melt and cold crstallization of PLA was promoted.The enzymatic degradation experiments indicated that the films had good biodegradability.These findings gave important implications for designing and manufacturing biodegradation package of high biological carbon content.