在42CrMo钢常规处理的基础上增加了冷处理,研究浅冷处理和深冷处理对42CrMo钢硬度和耐磨性的影响。结果表明,经浅冷处理和深冷处理后,42CrMo钢中残留奥氏体向马氏体发生转变,且碳化物析出增多,致使钢的硬度和耐磨性均有提升,且深冷处理后硬度和耐磨性提升幅度高于浅冷处理。
Based on the conventional treatment of 42CrMo steel,cryogenic treatment was added.Effects of shallow cryogenic treatment and deep cryogenic treatment on hardness and wear resistance of 42CrMo steel were studied.The results show that after shallow cryogenic treatment and deep cryogenic treatment,the retained austenite in 42CrMo steel transforms to martensite,and the precipitation of carbides increases,which leads to the improvement of hardness and wear resistance of the steel,and the improvement extent of hardness and wear resistance after deep cryogenic treatment is higher than that of shallow cryogenic treatment.
作者
张海东
闫献国
陈峙
赵敏娜
高源
李俊吉
李晋峰
高丽梅
Zhang Haidong;Yan Xianguo;Chen Zhi;Zhao Minna;Gao Yuan;Li Junji;Li Jinfeng;Gao Limei(School of Mechanical Engineering,Taiyuan University of Science and Technology,Taiyuan Shanxi 030024,China;Jinxi Axle Co.,Ltd.,Taiyuan Shanxi 030027,China)
出处
《金属热处理》
CAS
CSCD
北大核心
2020年第9期96-98,共3页
Heat Treatment of Metals
基金
国家自然科学基金(51675363)
太原科技大学博士启动基金(20182042)。
关键词
42CRMO钢
冷处理
硬度
耐磨性
微观组织
42CrMo steel
cryogenic treatment
hardness
wear resistance
microstructure