Hydrogen is a green clean fuel and chemical feedstock. Its separation and purification from hydrogencontaining mixtures is the key step in the production of hydrogen with high purity(>99.99%). In this work, carbon molecular sieve(CMS) membranes with ultrahigh permselectivity for hydrogen purification were fabricated by high-temperature(700–900 ℃) pyrolysis of polymeric precursor of phenolphthaleinbased cardo poly(arylene ether ketone)(PEK-C). The evolution of the microstructural texture and ultramicroporous structure and gas separation performance of the CMS membrane were characterized via TG-MS, FT-IR, XRD, TEM, CO2 sorption analysis and gas permeation measurements. CMS membranes prepared at 700 ℃ exhibited amorphous turbostratic carbon structures and high H2 permeability of 5260 Barrer with H2/CH4, H2/N2 and H2/CO selectivities of 311, 142, 75, respectively. When carbonized at900 ℃, the CMS membrane with ultrahigh H2/CH4 selectivity of 1859 was derived owing to the formation of the dense and ordered carbon structure. CMS membranes with ultrahigh permselectivity exhibit an attractive application prospect in hydrogen purification.
基金
the National Key R&D Program of China(2017YFB0603403)
National Natural Science Foundation of China(21676044,21878033,21978034)
High Level Innovation Team of Liaoning Province(XLYC1908033)
Fundamental Research Funds for the Central Universities(DUT19ZD211,DUT 2018TB02)for the financial support。