摘要
为了探究酚醛树脂刨花模压托盘的生产工艺,采用正交试验分析施胶量、热压温度和热压时间对模压托盘物理力学性能的影响。结果表明:在优化工艺参数:施胶量20%、热压温度200℃、热压时间10 min的条件制备的酚醛树脂模压托盘,含水率、密度、24 h吸水厚度膨胀率以及叉举抗弯性能均满足GB/T 30672—2014《模压平托盘植物纤维类》中一次性使用模压平托盘的相关要求。
The molded pallets were made from wood particles blended with phenolic formaldehyde adhesive.Effects of resin content,hot-press temperature and hot-press time on the physical and mechanical properties of molded pallets were investigated using an orthogonal design method.The the optimization of processing parameters was found at 20%of resin content,200℃ of hot-press temperature and 10 min of hot-press time.The moisture content,the density and the thickness swelling ratio after 24-hour water soaking and the bending resistance of molded pallets met the requirements of GB/T 30672—2014“Moulded flat pallets from plants fiber”respectively.
作者
杨飞
刘乐群
吴侨立
刘震涛
滑亚婷
YANG Fei;LIU Le-qun;WU Qiao-li;LIU Zhen-tao;HUA Ya-ting(Zhejiang Academy of Forestry,Hangzhou 310000,Zhejiang,China;Hangzhou Penno Packtech Co.Ltd,Hangzhou 310000,Zhejiang,China;Hangzhou Guoli Industrial and Trading Group Co.,Ltd.,Hangzhou 310000,Zhejiang,China)
出处
《木材工业》
北大核心
2020年第6期53-57,共5页
China Wood Industry
基金
杭州市主动设计重大专项“农林剩余物模压制备刨花成型托盘关键技术研究与产业化”(20172016A10)
浙江省省院合作重点专项“农林废弃物模压制备刨花成型托盘关键技术研究”(2017SY07)
国家标准项目“竹木刨花模压托盘通用技术条件”(20180966-T-432)
林业行业标准项目“模压托盘运输及使用要求”(2018-LY-012)。
关键词
模压托盘
酚醛树脂
施胶量
热压参数
力学性能
molded pallet
phenolic resin adhesive
resin content
hot-press parameter
mechanical properties