Cu matrix composites reinforced by TiB_(2)/TiN ceramic reinforcements(Cu/TBN composites)were prepared by hot pressing method.Prior to the hot pressing,Cu/TiB_(2)/TiN composite powders(CTBN powders),which were used as the starting materials of Cu/TBN composites,were fabricated by self-propagating high-temperature synthesis method.The CTBN particles were found to be in a special core–shell structure with a Cu–Ti alloy core and a TiB_(2)/TiN ceramic shell.The test results presented obvious improvements in mechanical properties.The highest ultimate tensile strength reached up to 297 MPa,77 MPa higher than that of Cu.And the highest hardness reached up to 70.7 HRF,15.7 HRF higher than that of Cu.A comparative study indicated that the core–shell structured particles could bring about more obvious strengthening eff ect than the traditional irregularly shaped particles,which was due to the improved Cu/ceramics interfacial bonding,the linkage strengthening effect of both TiB_(2) and TiN,and higher load bearing ability of the core–shell structured reinforcements.
基金
financially supported by the National Key R&D Program of China(No.2018YFF01013605)
the National Natural Science Foundation of China(No.51501215)
the Youth Innovation Promotion Association CAS(No.2019254)
the Science Foundation for Youth Scholar of State Key Laboratory of High Performance Ceramics and Superfine Microstructures(No.SKL201701)
the State Key Laboratory of New Ceramic and Fine Processing Tsinghua University(No.KF201806)。