CoO@CuO电极材料制备及超级电容性能研究

Preparation and Supercapacitor Performance of CoO@CuOElectrode Materials

超级电容器因具有功率密度高、充放电速率快、循环使用寿命长等优点而备受关注。CoO是一种优良的超级电容电极材料,理论比容量可以达到4292F·g^(-1),但其电导率较低,而且充放电过程中会产生体积膨胀,导致其实际比容量低于理论比容量。为此,本文首先采用热氧化法在泡沫铜导电集流体上生长CuO纳米线阵列,然后采用化学浴沉积法在CuO纳米线表面沉积CoO层级结构,制备核壳结构CoO@CuO电极材料。该电极材料在电流密度为2mA·cm^(-2)时的比容量可达到1.0430 F·cm^(-2)(117.1453 F·g^(-1)),并表现出了良好的电容保持率。

Supercapacitors have attracted attentions due to many advantages,such as ultra-high power density,fast and stable charge/discharge rate,long cycle life and so on.CoOis regarded as a promising electrode of supercapacitor,the theoretical specific capacity reaches 4292 F·g^(-1),but its low conductivity and volume expansion during charge/discharge process lead to very low actual specific capacity than the theoretical specific capacity.In order to solve these problems,CuOnanowire arrays were firstly grown on copper foams via the thermal oxidation method.And then,hierarchical CoOwas successfully deposited on CuOnanowires by chemical bath deposition,thus,core-shell CoO@CuOelectrode materials were obtained.This electrode materials have an excellent specific capacity of 1.0430 F·cm^(-2)(117.1453 F·g^(-1))at the current density of 2 mA·cm^(-2),as well as a good capacitance retention rate,which increase the number of surface active sites,reduce the effect of CoOvolume expansion.