研究了用脱硫石膏完全替代天然石膏制备嵌缝石膏,并解决嵌缝石膏薄批掉粉、表面强度低等质量通病。试验结果表明,当保水剂掺量为0.3%、可再分散乳胶粉掺量为1.2%、白水泥掺量为4%时,嵌缝石膏的抗压强度为18.0 MPa,抗拉强度为0.70 MPa、无裂缝、应用性能良好,综合性价比高。
This paper studied the preparation of caulking gypsum with 100%desulfurization gypsum instead of natural gypsum,and solved the common quality problems of caulking gypsum such as peeling off with thin layer and lower surface strength.When the content of water retaining agent,redispersible latex powder,and white cement is 0.3%,1.2%and 4%respectively,the compressive strength of the caulking gypsum is 18.0 MPa,the tensile strength is 0.70 MPa,the product has features of no cracks,excellent application performance and comprehensive cost-effective.
作者
徐建军
丁常正
赵大军
XU Jianjun;DING Changzheng;ZHAO Dajun(Jiangsu NIGAO Science of Technology Co.Ltd.,Changzhou 213141,China;Changzhou Architectural Research Institute Co.Ltd.,Changzhou 213015,China)
出处
《新型建筑材料》
2021年第1期52-53,92,共3页
New Building Materials
关键词
嵌缝石膏
脱硫石膏
涂层硬度
应用性能
caulking gypsum
desulfurization gypsum
coating hardness
application performance