摘要
采用固相烧结法制备一系列Er^3+单掺与Er^3+/Yb^3+共掺0.96Na0.5Bi0.5TiO3-0.04CaTiO3(NBT-CT∶xEr^3+/y Yb^3+,x=0.002~0.015,y=0.010)无铅压电陶瓷。通过X射线衍射仪和荧光光谱仪分别对样品的物相结构和上转换发光特性进行表征和分析。结果表明,样品的主晶相为NBT晶相。在波长为980 nm的近红外光激发下,Er^3+单掺与Er^3+/Yb^3+共掺NBT-CT陶瓷均呈现强的以绿光为主的Er^3+特征上转换发光。在NBT-CT∶xEr^3+中,当x=0.010时上转换发光性能最佳;Yb^3+能够起到敏化作用,明显增强Er^3+的上转换发光强度。
A series of Er^3+doped and Er^3+/Yb^3+co-doped 0.96Na0.5Bi0.5TiO3-0.04CaTiO3(NBT-CT∶x Er^3+/y Yb^3+,x=0.002~0.015,y=0.010)lead-free piezoelectric ceramics were prepared by a solid-state sintering method.The phase structure and up-conversion luminescence properties of the samples were characterized and analyzed by X-ray diffraction and fluorescence spectrofluorometer,respectively.These results show that the main crystal phase of the samples is that of NBT.Under the excitation of a 980 nm near-infrared light,the Er^3+doped and Er^3+/Yb^3+co-doped NBT-CT ceramics exhibit characteristic emission of Er^3+with strong dominant green up-conversion emissions.The optimal up-conversion luminescence performance with x=0.010 in NBT-CT∶x Er^3+ceramics are obtained.Yb^3+can act as sensitizer and significantly enhance the up-conversion luminescence intensity of Er^3+.
作者
马春林
周越
马晨宇
董倩文
吴瑾
范雨香
翟章印
MA Chunlin;ZHOU Yue;MA Chenyu;DONG Qianwen;WU Jin;FAN Yuxiang;ZHAI Zhangyin(School of Physics and Electronic and Electrical Engineering,Huaiyin Normal University,Huai'an 223300,China)
出处
《人工晶体学报》
EI
CAS
北大核心
2021年第1期138-142,共5页
Journal of Synthetic Crystals
基金
江苏省高等学校自然科学研究基金(19KJA150011)
淮安市自然科学研究计划(HAB202056)
江苏省高等学校大学生创新创业训练计划(201917011XJ,202010323074Y)。