This work focused on the role of Al_(2)O_(3) particles in the corrosion behavior of cold sprayed AA5083 aluminum alloy matrix composite(Al-MMC)coatings.The electrochemical characterization of the coatings was investigated in a 3.5 wt.%NaCl solution as a function of time.The results show that fragmentation of Al_(2)O_(3) particles is not clearly observed in the case of AA5083/20 vol.%Al_(2)O_(3) coating,while the broken Al_(2)O_(3) particles can be seen clearly in AA5083/40 vol.%Al_(2)O_(3) and AA5083/60 vol.%Al_(2)O_(3) coatings.The addition of 20 vol.%Al_(2)O_(3) particles yield the coating with the lowest porosity,and different volume fractions of Al_(2)O_(3)in the feedstock have important effects on the electrochemical behavior of composite coatings.The Al-MMC coating reinforced with 20 vol.%Al_(2)O_(3) particles exhibits the highest Ecorrand the lowest icorrcompared with the other conditions.The order of current density is as follows:AA5083/20vol.%Al_(2)O_(3)<AA5083<AA5083/40 vol.%Al_(2)O_(3)<AA5083/60 vol.%Al_(2)O_(3).
基金
financially supported by the authors would like to acknowledge the National Key Research and Development Program of China(No.2016YFB1100104)
the National Natural Science Foundation of China(No.51875470)
the State Key Laboratory of Solidification Processing(NPU,China)(No.2019-QZ-01)
the financial support from the fund of SAST(No.SAST2016043)。