基于AnyCasting软件,采用正交试验研究了压铸过程中冲头速率、模具温度、浇注温度对镁合金副车架铸件气孔含量、氧化倾向、冷隔和缩松等缺陷的影响,并得到了优化的压铸工艺参数:冲头速率为7m/s、模具温度为250℃、浇注温度为700℃。在该工艺参数条件下,获得了表面和内部品质良好的镁合金副车架压铸件,同时验证了通过模拟仿真优化压铸工艺参数方法的有效性。
The effects of injection rate,mold temperature and pouring temperature on porosity,oxidation tendency,cold-shut and shrinkage porosity in the Mg subframe castings were investigated by using AnyCasting software and orthogonal test method.The optimized die casting process parameters were presented as follows:injection rate of 7 m/s,mold temperature of 250℃,pouring temperature of 700℃.Under these process parameters,Mg subframe castings with sound surface and internal quality were produced by die casting process,and the effectiveness of optimizing the casting process parameters by simulation was also verified.
作者
付彭怀
丁浩源
李德江
王泽忠
赵正江
周力
朱胜利
丁胜长
刘锡林
彭立明
Fu Penghuai;Ding Haoyuan;Li Dejiang;Wang Zezhong;Zhao Zhengjiang;Zhou Li;Zhu Shengli;Ding Shengchang;Liu Xili;Peng Liming(National Engineering Research Center of Light Alloy Net Forming\School of Materials Science and Engineering,Shanghai Jiaotong University;Dongfeng Automobile Company Technology Center;Fengyang Light Alloy Net Forming National Engineering Research Center Co.,Ltd.)
出处
《特种铸造及有色合金》
CAS
北大核心
2021年第2期231-235,共5页
Special Casting & Nonferrous Alloys
基金
国家重点研发计划资助项目(2016YFB0301002)
国家自然科学基金资助项目(51821001)
宁波市科技创新2025重大专项资助项目(2019B10102)。
关键词
镁合金
副车架
压铸
铸造仿真
正交试验
Mg Alloy
Subframe
Die Casting
Casting Simulation
Orthogonal Test