在生产过程中采用树脂砂轮打磨+酸洗工艺对Zr-3合金板坯进行表面处理后,发现其表面出现白斑。采用化学成分分析、显微组织观察和残余应力测试方法对白斑产生原因进行了分析。结果表明:白斑是由于过高的残余应力产生的;通过改用千叶轮打磨或喷砂工艺,降低表面残余应力,减少孪晶形成后,白斑缺陷消除。
After surface treatment by resin wheel grinding and pickling in production,white spot appeared on surface of Zr-3 alloy slabs.The cause of the white spot was analyzed by chemical composition analysis,microstructure observation and residual stress test.The results show that the white spot was caused by excessive residual stresses.The white spot defect was eliminated by application of thousand impeller grinding or sand blasting to decrease surface residual stresses and reduce twin crystal formation.
作者
岳强
徐滨
胡旭坤
赵林科
YUE Qiang;XU Bin;HU Xukun;ZHAO Linke(Research and Development Center for National Energy Nuclear Grade Zirconium,Nuclear Grade Zirconium Key Laboratory in Shaanxi,State Nuclear Bao Ti Zirconium Industry Company,Baoji 721013,China)
出处
《机械工程材料》
CAS
CSCD
北大核心
2020年第12期103-106,共4页
Materials For Mechanical Engineering
关键词
Zr-3合金
表面处理
白斑缺陷
残余应力
孪晶
Zr-3 alloy
surface treatment
white spot defect
residual stress
twin crystal