摘要
To improve the interfacial conductivity and corrosion resistance of AISI430 stainless steel(430 SS)as bipolar plates for direct formic acid fuel cells(DFAFCs),a Nb_(0.8)Zr_(0.2) layer has been successfully synthesized via the pulsed laser deposition(PLD)technique on the surface of 430 SS.This Nb_(0.8)Zr_(0.2) layer is smooth,uniform,and comparatively compact without any surface flaw and micropore.Investigation under the simulated anodic environment of DFAFCs(0.05 M H_(2)SO_(4)+2 ppm HF+10 M HCOOH at 70℃)shows that the corrosion resistance of 430 SS is obviously ameliorated after the PLD modification.In addition,the interfacial contact resistance of Nb_(0.8)Zr_(0.2)-430 SS(6.0 mΩcm^(2))is much smaller than that of bare 430 SS(151.3 mΩcm^(2))at the clamping force of 140 N cm^(-2).Besides,diff erent from the highly increased interfacial contact resistance of bare 430 SS,the Nb_(0.8)Zr_(0.2)-430 SS shows a minor increase resistance after potentiostatic tests in simulated anodic environment of DFAFCs.
基金
financially supported by the National Natural Science Foundation of China(Nos.51962027,51974167,21968022,and 21868022)
the Natural Science Foundation of Inner Mongolia(No.2019BS02002)
the Project of Science Foundation of the Educational Department of Inner Mongolia(No.NJZY19135)
the Inner Mongolia University of Science and Technology Innovation Fund(No.2019QDL-B23)。