The effect of hydro gen charging on microstructural evolution and corrosion behavior of a Ti-4Al-2V-1Mo-1Fe alloy in a 3.5 wt.% NaCl solution was investigated.The results showed that the hydrogen charging induced the formation and growth of γ-TiH and δ-TiH_(2) phases,leading to the initiation and propagation of hydrogen-induced cracks.It was also found that hydrogen charging can change the passivity of this alloy and increase its pitting corrosion susceptibility.The main reason for these was attributed to the fo rmation of hydrides in α phase in the Ti-4Al-2V-1Mo-1Fe alloy,leading to the preferential dissolution of the α phase and thus the deterioration in the protective ability of passive film.