Lithium-sulfur(Li-S)batteries are receiving increasing attention as one of the potential next-generation batteries,owing to their high energy densities and low cost.However,practical Li-S batteries with high energy densities are extremely hindered by the sulfur loss,low Coulombic efficiency,and short cycling life originating from the polysulfide(LiPS)shuttle.In this study,two-dimensional(2D)ZnCo_(2)O_(4) microsheets fabricated by a facile hydrothermal process are employed to modify the separator,for improving the electrochemical performances of Li-S cells.The resulting 2D Zn Co_(2)O_(4)-coated separator features a coating thickness of approximately 10 lm,high ionic conductivity of 1.8 m S/cm,and low mass loading of 0.2 mg/cm^(2).This 2D ZnCo_(2)O_(4)-coated separator effectively inhibits Li PS shuttle by a strong chemical interaction with Li PS as well as promotes the redox kinetics by Zn CO2O4-coated layers,as determined by X-ray photoelectron spectroscopy analysis,self-discharge,time-dependent permeation test,Li symmetric cell test,and Li2S nucleation analyses.Consequently,the Li-S batteries based on the 2D Zn Co_(2)O_(4)-coated separator exhibit a high initial discharge capacity of 1292.2 m Ah/g at 0.1 C.Moreover,they exhibit excellent long cycle stability at 1 and 2 C with capacity retention of 84%and 86%even after800 cycles,corresponding to a capacity fading rate of 0.020%and 0.016%per cycle,respectively.Effectively,these Li-S cells with a high sulfur loading at 5.3 mg/cm^(2) and low electrolyte concentration of 9 l L/mg deliver a high discharge capacity of 4.99 m Ah/cm^(2) after 200 cycles at 0.1 C.
基金
supported by a grant from R&D Program of the Korea Railroad Research Institute,Republic of Korea。