In this paper,new improvements of methodological concepts upon examining wettability of high vapor pressure liquid metal systems(e.g.Mg-based alloys)in contact with refractory materials,are presented and discussed.In this regard,high-temperature experiments on molten magnesium(Mg)in contact with graphite as a refractory substrate,were performed by utilizing a newly developed testing device and by applying a suitable experimental procedure.The wetting experiments were carried out by the sessile drop method and under identical testing conditions(700℃/10 min under a protective gas atmosphere).Two different procedures were applied:the classical contact heating(CH)or a newly introduced capillary purification(CP)one.The contact angle behaviors observed under the same conditions were strongly influenced by the applied procedure.Specifically,in the case of using the CH procedure,a presence of native surface oxide layer on the metal surface hinders the observations of melting process,making not possible to experimentally determine the wetting kinetics curveθ=f(t).Contrarily,during the wetting test performed on the Mg/graphite couple by applying the CP procedure,the native surface oxide layer was mechanically removed during the squeezing of the molten Mg through the hole of a capillary.Indeed,an oxide-free squeezed Mg-drop with regular and spherical shape was successfully obtained and dispensed on the graphite substrate.Consequently,the reliable contact angle value aroundθ=150°for the Mg/graphite system,was measured within the wetting test.
基金
The studies were performed within the financial support given by the National Science Centre(NCN)in Poland,un-der the project MINIATURA 2,No.2018/02/X/ST8/03044 in.2019-2020.