采用强流脉冲离子束辐照的改性方法研究了其对Ti Al N涂层刀具的表面改性效果。使用1.5、2.3 J/cm2的强流脉冲离子束对试样进行1、5、10次辐照实验。结果表明,试样表层产生大量龟裂状裂纹。随着辐照次数和脉冲能量的增加,试样表层微裂纹逐渐减少,取而代之的是沸腾状的烧蚀孔洞。辐照后,试样的表面显微硬度和耐磨性均得到了提高,试样的表面显微硬度最高提高了24.9%,耐磨性最高提高了25.5%。
The modified method of high intense pulsed ion beam(HIPIB) irradiation was used to research its effects on the surface of Ti Al N coated tool. The cutting sample was irradiated by HIPIB at the energy densities of 1.5 J/cm2 and 2.3 J/cm2 and shot numbers of 1, 5 and 10 pulse. The results show that the surface of the sample generates a large number of cracks.With the increase of irradiation times and pulse energy, the micro-cracks on the sample surface gradually decrease, which is replaced by boiling holes. After irradiation, the surface microhardness and wear resistance of the sample improve. The microhardness of the sample surface increases by 24.9% in maximum, and the wear resistance increases by 25.5% in maximum.
作者
董艇舰
倪振飞
武庆余
DONG Tingjian;NI Zhenfei;WU Qingyu(Examination Administration,Civil Aviation University of China,Tianjin 300300,China;College of Aeronautical Engineering,Civil Aviation University of China,Tianjin 300300,China)
出处
《热加工工艺》
北大核心
2021年第6期75-78,共4页
Hot Working Technology
基金
“大型航空发动机机匣加工及测量成套装备研制”科技重大专项课题(2013ZX04001071)
中国民航大学科研启动基金项目(05QD07Q)。
关键词
强流脉冲离子束
表面改性
裂纹
显微硬度
耐磨性
high intense pulsed ion beam
surface modification
crack
microhardness
wear resistance