摘要
针对同轴送粉的激光定向能量沉积(DED),结合送粉方程与VOF(Volume of Fluid)方法,提出了沉积层计算模型,采用固定坐标系下的移动边界条件,对单道IN718成形过程进行了实时模拟,并进行了实验验证。结果表明:在单层单道沉积加工下,随着扫描速度从8 mm·s^(-1)增加到14 mm·s^(-1),沉积层高度和宽度分别减小了57.1%和21.6%,计算所得沉积层高度、宽度及熔深与实验结果吻合良好。在此基础上,计算了在单向平行搭接方式下搭接率为30%的单层双道沉积层温度场分布,得到了不同搭接时刻沉积层的温度变化规律。受第一沉积层热累积的影响,熔池潜热效应会使搭接加工时的表面最高温度略低于单道加工时的表面最高温度;同时受搭接沉积层在扫描过程中高温状态的影响,第一沉积层在搭接扫描过程中会出现回温现象,回温区间为1000~1600 K,幅度为100~300 K。该研究成果对深入理解同轴送粉激光定向能量沉积工艺机理以及工艺优化具有重要意义。
Objective During the coaxial powder feeding laser deposition process,the mass transfer,heat transfer,and fluid flow in the molten pool are closely related to the surface and internal quality of the formed part.Numerical simulation technology can provide an effective means for studying this series of coupled complex physical phenomena.In recent years,numerical modeling of powder feeding laser deposition has made great progress.However,the deposition layer morphologies in such model are mostly pre-set rather than being computed.In fact,the establishment and development of the deposition layer morphology is a combined result of powder feeding,melting,and solidification.During the development of the technology towards precision manufacturing,it is of great significance for understanding the deposition mechanism and improving the internal and surface quality of the parts to build a coupled mathematical model that can accurately describe the deposition formation and the physical processes in the molten pool.In this paper,a mathematical model of the coaxial powder feeding laser deposition is established,and the numerical computation of the single pass and overlap forming processes is completed.The shape of the deposition layer,the characteristics,and the cause of the temperature field of the molten pool are analyzed.We hope that this research can provide help for understanding the deposition mechanism dominating the forming process,which promotes laser deposition manufacturing towards high dimensional accuracy and high internal quality.Methods In this study,a three-dimensional mathematical model of the coaxial powder feeding laser deposition is established by combining the volume of fluid(VOF)method with the powder feeding equation.The shape of the deposition layer and the morphology of the molten pool of single pass and overlap forming processes for IN718 alloy are simulated and verified by experiments with the same parameters.Based on the good agreement between the simulation results and the experimental results,the mutual influence of the temperature between the first pass deposition and the overlap pass deposition for the overlap forming is evaluated.The heat accumulation effect due to the first pass deposition on the temperature of the overlap and its molten pool is analyzed by comparing their maximum temperatures.At the same time,the effect of the current high temperature of the overlap pass deposition on the temperature gradient and cooling rate of the first pass deposition is analyzed by comparing temperature rerising.The potential effect of the first pass deposition on the solid phase transition is also pointed out.Results and Discussions The shape and size of the deposition layer of single pass forming are achieved by using the three-dimensional mathematical model presented in this paper,which are further compared with the experimental results(Fig.4 and Fig.5);the temperature field and the development of the three-dimensional molten pool morphology under different moments are obtained(Fig.7 and Fig.8);the molten pool depth calculated by the simulation is basically consistent with the experimental results(Fig.9).On the basis of single pass forming simulation,the deposition layer shape,molten pool morphology,and temperature field are obtained for overlap forming process with 30%overlapping rate(Fig.10,Fig.11 and Fig.12).Because of the thermal accumulation of the first pass deposition,the molten pool of the overlap pass deposition is 4.19%larger than that of single pass process and absorbs more latent heat of fusion,which leads to that the maximum surface temperature of the overlap pass deposition is slightly lower than that of the single pass forming(Fig.13 and Fig.14).At the same time,affected by the high temperature state of the overlap pass deposition,the temperature of the first pass deposition re-rises in the range of 1000-1600 K,and the amplitude is 100-300 K(Fig.16).Conclusions In this paper,a three-dimensional mathematical model is put forward by combining the VOF method with the powder feeding equation,and the simulations of single pass and overlap laser deposition forming processes with coaxial powder feeding are realized.When the scanning speed is increased by 75%,that is,from 8 mm/s to14 mm/s,the height and width of the deposition layer are reduced by 57.1%and 21.6%,respectively.The calculated height,width,and depth of the single pass deposition are in good agreement with the experimental results.In the overlap forming process with 30%overlapping rate for one-way parallel scanning,influenced by the heat accumulation of the first pass deposition,the molten pool formed by the overlap pass deposition is 4.19%larger than that formed by the single pass forming,and more latent heat of fusion is absorbed,which causes that the highest surface temperature of 2038 K during the overlap forming is slightly lower than that of 2068 K during single pass forming.At the same time,the first pass deposition is also affected by the high temperature state of the overlap,which presents the temperature re-rise to some extent at different positions.Because the temperature re-rise occurs within 1000-1600 K with an amplitude of 100-300 K,the solid phase transition of the first pass deposition will be affected for IN718 alloy.The results of this study are of great significance for process optimization and quality improvement in laser deposition technology.
作者
王予
黄延禄
杨永强
Wang Yu;Huang Yanlu;Yang Yongqiang(School of Mechanical and Automotive Engineering,South China University of Technology,Guangzhou,Guangdong 510640,China)
出处
《中国激光》
EI
CAS
CSCD
北大核心
2021年第6期179-190,共12页
Chinese Journal of Lasers
基金
国家自然科学基金(51705160)
广东省重大专项(2018B090905001)。
关键词
激光技术
同轴送粉
数值模拟
沉积层形状
温度场
laser technique
coaxial powder feeding
numerical simulation
deposition layer shape
temperature field