摘要
Based on the synchrotron soft X-ray absorption spectroscopy experiments,the fundamental electronic structures of layered Li NixCoyMnzO_(2)(NCM)are investigated systematically and the data of transitionmetal(TM)L-and O K-edges spectra are collected.Distribution of Ni ions under different oxidation states is evaluated according to linear combination fit.It is found that the ratio of Ni^(4+)expands with the increase of Ni since it dominates in charge compensation during charging,and that the existence of Ni^(3+)is nearly negligible in delithiated NCM.The valence state of Co also strongly depends on Ni content,the perceptible position shift of Co L_(3)-edge absorption peak towards higher energy in Ni-rich material agrees well with the small voltage plateau at around 4.2 V.The stability of Mn is verified as no obvious spectral change with the Mn L-edge is observed.Moreover,as Ni content rises,the O 2p holes near the Femi level increases with higher oxidation state of Ni,indicating the enhanced hybridization of O 2p-TM 3 d.Delithiated NCMs with higher Ni content are prior to lose electron existing in highly hybridized Ni3 dO 2 p bands upon heating,which accounts for the pronounced O_(2)release in phase transitions and the deterioration in thermal stability.These detailed observation of the electronic structure evolution is one of the key ingredients to improving the electrochemical and thermal performance of NCM.
基金
supported by the National Natural Science Foundation of China(No.51976209)
the Fundamental Research Funds for the Central Universities(No.WK2320000040)
supported by the Youth Innovation Promotion Association CAS(No.Y201768)。