HRB400E热轧带肋钢筋黑线成因分析

Cause analysis of black lines on HRB400E hot rolled ribbed bar

针对某厂某一批次直径为Φ28 mm的HRB400E热轧带肋钢筋表面出现黑线的现象,利用金相显微镜、扫描电镜和X射线能谱仪对黑线试样进行观察和分析。结果表明,HRB400E钢筋表面黑线的产生,主要是由于结晶器保护渣或中间包覆盖剂卷入连铸坯以及浸入式水口熔损造成的复合型非金属夹杂物分布于钢坯中,钢筋在轧制过程中由于应力作用,在夹杂物边部产生裂纹,并随轧制的进行,裂纹进一步扩展、暴露,进而在钢筋表面形成黑线。经过优化连铸工艺参数,黑线基本得到了控制。

In view of the phenomenon of black lines existing on the several batches of HRB400E hotrolled ribbed bar with a diameter of 28 mm,the samples had been checked and analyzed by optical microscope,scanning electron microscope and energy dispersive spectrometer.The results show that the main reason for black line is the existence of compound type inclusions formed by mold flux or tundish covering agent involving continuous cast billet and the liquate of the submersed nozzles,which distribute in billet.As a result of stress effect,the cracks grow along the inclusions and propagate during the rolling.The black lines on the HRB400E hot-rolled ribbed bar can be effectively eliminated by optimizing the process parameters of continuous casting.