摘要
Y_(2)O_(3) is regarded as one of the potential environmental barrier coating(EBC)materials for Al_(2)O_(3)f/Al_(2)O_(3)ceramic matrix composites owing to its high melting point and close thermal expansion coefficient to Al_(2)O_(3).However,the relatively high thermal conductivity and unsatisfactory calcium-magnesium-aluminosilicate(CMAS)resistance are the main obstacles for the practical application of Y_(2)O_(3).In order to reduce the thermal conductivity and increase the CMAS resistance,four cubic bixbyite structured high-entropy oxides RE_(2)O_(3),including(Eu_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3),(Sm_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3),(Sm_(0.2)Eu_(0.2)Er_(0.2)Y_(0.2)Yb_(0.2))2O_(3),and(Sm_(0.2)Eu_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3)were designed and synthesized,among which(Eu_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3)and(Sm_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3)bulks were prepared by spark plasma sintering(SPS)to investigate their mechanical and thermal properties as well as CMAS resistance.The mechanical properties of(Eu_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3)and(Sm_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3) are close to those of Y_(2)O_(3) but become more brittle than Y_(2)O_(3).The thermal conductivities of(Eu_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb_(0.2))2O_(3) and(Sm_(0.2)Er_(0.2)Lu_(0.2)Y_(0.2)Yb02)2O_(3)(5.1 and 4.6 W·m^(-1)·K^(-1))are only 23.8%and 21.5%respectively of that of Y_(2)O_(3)(21.4 W·m^(-1)·K^(-1)),while their thermal expansion coefficients are close to those of Y_(2)O_(3) and A12O_(3).Most importantly,HE RE_(2)O_(3) ceramics exhibit good CMAS resistance.After being attacked by CMAS at 1350℃for 4 h,the HE RE_(2)O_(3) ceramics maintain their original morphologies without forming pores or cracks,making them promising as EBC materials for Al_(2)O_(3)f/Al_(2)O_(3) composites.
基金
This work was financially supported by the National Natural Science Foundation of China under Grant Nos.51972089,51672064,and U1637210.