This study analyzes the effect of substitution of Ni for Zn on microstructure and mechanical properties of Mg-Gd-Y-Zn-Mn alloy.Our results show that the volume fraction of Mg5(Gd,Y)and(Mg,Zn)3RE phase decreased and LPSO phase increased with more substitution of Ni.After homogenization,onlyα-Mg and LPSO phase existed.In Mg-Gd-Y-Zn-Mn alloys,the LPSO phases mainly consisted of the 14H type.While in Mg-Gd-Y-Ni-Mn alloy,the LPSO phases consisted of the 18R type.In addition,compared with Mg-Gd-Y-Zn-Mn alloy,the mechanical properties of as-extruded Ni-substitution alloys were improved due to the better refinement of the size of grains and LPSO phases.The tensile strength in as-extruded Mg-Gd-Y-Ni-Mn alloy could reach up to 400 MPa with 18%of the elongation to failure.
基金
supported by the National Key Research and Development Program of China(No.2016YFB0301100)
the Natural Science Foundation Commission of China(Grant No.51571044)
Chongqing foundation and advanced research project(Grant No.cstc2015jcyjBX0081)
the National Basic Research Program of China(Grant No.2013 CB632201)。