摘要
In the present study,the non-isothermal early stages of surface oxidation of liquid Mg-1%Y alloy during casting were studied under UPH argon,dry air,and air mixed with protective fluorine-bearing gases.The chemistry and morphology of the surface films were characterized by SEM and EDX analyses.The results indicate a layer of smooth and tightly coherent oxidation film composed of MgO and Y_(2)O_(3) formed on the molten Mg-Y alloy surface with 40-60 nm thickness under dry air.A dendritic/cellular microstructure is clearly visible with Y-rich second phases gathered in surface of the melt and precipitated along the grain/cell boundaries under all gas conditions.Under fluorine-bearing gas mixtures,the surface film was a mixed oxide and fluoride and more even;a flat and folded morphology can be seen under SF6 with oxide as dominated phase and under 1,1,1,2-tetra-fluoroethane,a smooth and compact surface film uniformly covering the inner surface of the bubble with equal oxide and fluoride thickness,which results in a film without any major defects.MgF_(2) phase appears to be the key characteristic of a good protective film.