Improved mechanical proprieties of“magnesium based composites”with titaniume-aluminum hybrids

In this study,the effect of micron-sized titanium and aluminum addition on the microstructural,mechanical and work-hardening behavior of pure Mg is investigated.Pure Mg reinforced with 10%Ti and 10%Ti-1%Al particulates were synthesized through semi-powder metallurgy route followed by hot extrusion.Semi-powder metallurgy appears to be promising approach for the synthesis of Mg based composite,as it is free of ball milling.Tensile results indicate that the direct addition of micron-sized 10wt.%titanium particulates to pure Mg,caused an improvement in elastic modulus,0.2%yield strength,ultimate tensile strength,and failure strain(+72%;+41%;+29%;and+79%respectively).The addition of micron-sized 10wt.%titanium particles along with 1.0wt.%Al particles to pure Mg,resulted in an enhancement in elastic modulus,0.2%yield strength,ultimate tensile strength,and failure strain(+74%;+56%;+45%;and+241%respectively).Besides tensile test,Vickers hardness and work-hardening behavior of prepared composites were also examined.Impressive failure strain of Mg-10Ti-1Al composite can be attributed to the better compatibility of Ti particulates with Mg due to presence of alloying element Al.