摘要
A single Si_(1−x)C_(x)coating and compound coatings were deposited on Mg-3Sn matrix alloy by magnetron sputtering method.Compound coatings included Mg or Mg/AlTi intermediates between Mg-3Sn substrate and Si_(1−x)C_(x)coating.The thermal conductivity of the Mg-3Sn alloy after coating was enhanced at room temperature.The results showed that the Mg-3Sn alloy coated with Mg/AlTi/Si_(1−x)C_(x)displayed higher thermal conductivity,its thermal conductivity after corrosion was 90.1 W/(m K)and 108.4 W/(m K)at 25℃and 100℃,respectively.Meanwhile,it was revealed that the Mg/Si_(1−x)C_(x)and Mg/AlTi/Si_(1−x)C_(x)compound coatings had nobler Ecorr and much lower i_(corr),higher Rp,compared with the bare Mg-3Sn and Mg-3Sn/Si_(1−x)C_(x)system,and improved the corrosion resistance of the magnesium substrate.