Large magnetic entropy change and adiabatic temperature rise of a ternary Gd_(34)Ni_(33)Al_(33) metallic glass

A low cost Gd_(34)Ni_(33)Al_(33) metallic glass with excellent magnetocaloric properties was successfully prepared in the present work.The magnetic properties of the ribbons were measured by constructing the relationship of magnetic entropy change(-ΔS_(m)) on temperature as well as magnetic field.The amorphous alloy shows typical magnetocaloric behaviors,large maximum-ΔS_(m)(11.06 J/(kg·K) under 5 T)and adiabatic temperature rise(4.3 K under 5 T) near 40 K,indicating that the low cost Gd_(34)Ni_(33)Al_(33) metallic glass is a good candidate material for low temperature magnetic refrigeration.