摘要
So far,only two orientation relationships(OR)between hexagonal close-packed(HCP)(αphase)and facecentered cubic(FCC)structures in zirconium and titanium alloys have been reported.Here a new type FCC phase(named γ phase)with OR:<11■0>_(α)‖<100>_(γ) and{0001}_(α)‖{002}_(γ) was observed for the first time in annealed pure zirconium by means of transmission electron microscopy(TEM)technique.The α→γ phase transformation can be accomplished via expansion along[1■00]direction and slip of Shockley partial dislocation with 1/3[1■00]on(0001)basal planes.