Synthesis of Lignin-based Nonisocyanate Poly(imine-hydroxyurethane)s Networks.Part II:Self-healing,Reprocessing,and Degradation

This study provides a comprehensive understanding of the polymeric properties of lignin-based non-isocyanate poly(iminehydroxyurethane)s(LNIPUs).The properties of the LNIPUs are affected by changes in the stoichiometric feed ratios of the bis(6-membered cyclic carbonate)(BCC)and levulinate enzymatic hydrolysis lignin(LEHL).The results showed that the LNIPUs exhibited a short relaxation time and excellent thermal repair and degradation properties.With a change in the LEHL content in the LNIPUs to 45.53%,a relaxation time of only 9 s was achieved,and the thermal repair rate of the scratches reached 93%.Furthermore,the tensile strength of the LNIPUs decreased with an increase in the LEHL content after two hot-pressing processes,while a higher than 75% tensile strength was maintained after the second hot-pressing treatment.The LNIPUs exhibited thermoresponsive shape memory property with deformation and shape fixing at 80℃.In addition,the as-synthesized LNIPUs were soluble in ethylene glycol in the absence of any organic solvents.This work demonstrates the synthesis of LNIPUs with self-healing,reprocessing,shape memory,and degradation properties.