Room temperature preparation of highly stable cesium lead halide perovskite nanocrystals by ligand modification for white lightemitting diodes

The poor stability of halide perovskite nanocrystals(NCs)has severely hindered future practical application.Herein,we proposed a facile and effective ligand modification route to synthesize stable CsPbBr_(3) nanocrystals by introducing a double-terminal ligand,namely 4,4'-Azobis(4-cyanovalericacid)(CA),to replace the conventional oleic acid(OA)ligand at room temperature.The as-synthesized CsPbBr_(3)-CA not only possesses high photoluminescence quantum yield(72%)related to the reduced trap defects,but also shows significantly improved stability exposure to water,ethanol,light,and/or heat benefiting from the CA ligand anchored to NC surfaces tightly.The photoluminescence intensity of CsPbBr_(3)-CA maintains about 80%and 75%of its initial emission intensity after immersed in water or ethanol for 360 min,respectively,whereas that of the CsPbBr_(3)-OA was quenched completely within a few minutes.Moreover,an all-inorganic white light-emitting diode(LED)covered 126%National Television System Committee(NTSC)standard and 92%Rec.2020 standard was fabricated by combining the green CsPbBr_(3)-CA and commercial red-emitting K2SiF6:Mn4+(KSF)phosphors onto a blue LED chip.Thus,the presented work initiates the development of the room temperature preparation of high quality CsPbBr_(3) and shows prospect for next-generation displays.