摘要
In this study,AleCuO nanocomposites were fabricated by sol-gel method.As a contrast,the thermite was prepared by physical mixing at the equivalence ratio of 0.5,1,2,respectively.The intermediates and samples as prepared were characterized by SEM and XRD.The exothermic properties of the two samples prepared at different equivalence ratios were tested and the reaction products were characterized by XRD.The SEM results show that the sample prepared by the sol-gel method demonstrates a micron-sized agglomerated sphere formed by a mutual wrapping of Al NPs and CuO NPs,and the particles are evenly distributed in the agglomerate.In addition,when the content of Al powder is seriously insufficient,the heat release of the sample prepared by physical mixing is 1.6 times that of by sol-gel method.With the increase of Al powder content,the exothermic properties of Al/CuO NPs prepared by sol-gel method began to increase significantly compared with physical mixing and the difference is 1.5 times when the equivalence ratio increases to 2.It can be concluded that the reason for this result may be attributed to the different mass transfer modes of components due to the different morphologies of samples.